Assessment of Native Human Articular Cartilage: A Biomechanical Protocol

Objectives: Recapitulating the mechanical properties of articular cartilage (AC) is vital to facilitate the clinical translation of cartilage tissue engineering. Prior to evaluation of tissue-engineered constructs, it is fundamental to investigate the biomechanical properties of native AC under sudden, prolonged, and cyclic loads in a practical manner. However, previous studies have typically reported only the response of native AC to one or other of these loading regimes. We therefore developed a streamlined testing protocol to characterize the elastic and viscoelastic properties of human knee AC, generating values for several important parameters from the same sample. Design: Human AC was harvested from macroscopically normal regions of distal femoral condyles of patients (n = 3) undergoing total knee arthroplasty. Indentation and unconfined compression tests were conducted under physiological conditions (temperature 37 °C and pH 7.4) and testing parameters (strain rates and loading frequency) to assess elastic and viscoelastic parameters. Results: The biomechanical properties obtained were as follows: Poisson ratio (0.4 ± 0.1), instantaneous modulus (52.14 ± 9.47 MPa) at a loading rate of 1 mm/s, Young’s modulus (1.03 ± 0.48 MPa), equilibrium modulus (7.48 ± 4.42 MPa), compressive modulus (10.60 ± 3.62 MPa), dynamic modulus (7.71 ± 4.62 MPa) at 1 Hz and loss factor (0.11 ± 0.02). Conclusions: The measurements fell within the range of reported values for human knee AC biomechanics. To the authors’ knowledge this study is the first to report such a range of biomechanical properties for human distal femoral AC. This protocol may facilitate the assessment of tissue-engineered composites for their functionality and biomechanical similarity to native AC prior to clinical trials.