Flexural properties of z-pinned laminates

This paper examines the effect of pinning on the flexural properties, fatigue life and failure mechanisms of carbon/epoxy laminates. Five-harness satin weave carbon/epoxy laminates were reinforced in the through-thickness direction with different volume fractions and sizes of fibrous composite pins. Microscopic examination of the laminates before flexural testing revealed that the pins caused considerable damage to the microstructure, including out-of-plane crimping, in-plane distortion and breakage of the fibres and the formation of resin-rich zones around each pin. The pins also caused swelling of the laminate that reduced the fibre volume content. Despite the damage, the pins did not affect the flexural modulus of the laminate. However, increasing the volume content or diameter of the pins caused a steady decline in the flexural strength and fatigue life, which appear to be governed by fiber rupture on the tensile side of the laminate. Property changes are discussed in terms of transitions in the dominant failure mechanisms due to the presence of pins.