High resolution microstructure characterization of the interface between cold sprayed Al coating and Mg alloy substrate

High-resolution transmission electron microscopy (HR-TEM) has validated the intimate metallurgical (atomic) bond formed along the interface of a cold-sprayed Al coating upon an Mg-alloy (AZ91) substrate. The compressive impact led to the formation of nanostructured layers of about 300-500 nm into the substrate. A highly distorted lattice structure with the inclusion of small amorphous zones was observed at the periphery of the particle/substrate interface, as a result of adiabatic shear plastic deformation at a high strain rate.